UPMSP Vocational Ceramics study materials
UPMSP Vocational Ceramics study resources

UPMSP Vocational Ceramics practice questions

One question at a time. Build your UPMSP Vocational Ceramics understanding.

First 50 of 200 questions. Each one lists the choices, the correct answer, and an explanation. The checker at the top of this page saves progress in this browser when it is available.

Continue in the practice tool above to load more questions, 50 at a time.

Question 1Ceramic Raw Materials and Clay Bodies

Which clay mineral is the main constituent of the plastic clay fraction used in ceramic bodies?

  1. Feldspar
  2. Quartz
  3. Kaolinite Correct answer.
  4. Calcite

Explanation

Kaolinite is a layered aluminium silicate hydrate that gives clay its plasticity and is the dominant mineral in most plastic ceramic clays. Quartz and feldspar are non-plastic ingredients added as filler and flux, and calcite is a carbonate flux or whiting used in glazes.

Question 2Ceramic Raw Materials and Clay Bodies

What is the approximate temperature range at which kaolin loses its chemically combined water during firing?

  1. 900-1000 C
  2. 1200-1300 C
  3. 100-150 C
  4. 450-600 C Correct answer.

Explanation

Dehydroxylation of kaolinite, the loss of structural OH groups, occurs roughly between 450 and 600 degrees Celsius and converts kaolinite into metakaolin. This endothermic reaction is distinct from the later mullite formation and vitrification stages.

Question 3Ceramic Raw Materials and Clay Bodies

A potter needs a clay body with high plasticity for throwing tall forms. Which additive most directly improves workability?

  1. Whiting
  2. Fine silica sand
  3. Coarse grog
  4. Bentonite Correct answer.

Explanation

Bentonite is a highly plastic montmorillonite clay that is added in small amounts to boost plasticity and green strength in lean bodies. Grog and sand are non-plastic and reduce plasticity, while whiting acts as a flux.

Question 4Ceramic Raw Materials and Clay Bodies

Which material is commonly added to a clay body to reduce drying shrinkage and firing shrinkage?

  1. Ball clay
  2. Sodium silicate
  3. Grog Correct answer.
  4. Bentonite

Explanation

Grog is crushed fired ceramic material that is already shrunk, so it acts as a non-shrinking skeleton and lowers overall shrinkage. Bentonite and ball clay increase plasticity and shrinkage, and sodium silicate is a deflocculant for casting slips.

Question 5Ceramic Raw Materials and Clay Bodies

In a slip-casting body, what is the role of sodium silicate?

  1. It increases the fired strength of the cast piece.
  2. It flocculates the slip to make it thicker.
  3. It deflocculates the slip so it flows with less water. Correct answer.
  4. It lowers the maturing temperature of the glaze.

Explanation

Sodium silicate is an alkali deflocculant that increases the negative surface charge on clay particles, causing them to repel and disperse. This allows a high-solids slip to flow with much less water, improving casting behaviour and reducing shrinkage.

Question 6Ceramic Raw Materials and Clay Bodies

Which oxide is regarded as the principal flux in high-temperature porcelain bodies?

  1. Potassium oxide Correct answer.
  2. Zirconia
  3. Alumina
  4. Silica

Explanation

Potassium oxide, supplied by potash feldspar, lowers the melting point and promotes vitrification of porcelain at high temperature. Alumina and silica are network formers that raise refractoriness, and zirconia is a refractory or opacifying oxide.

Question 7Ceramic Raw Materials and Clay Bodies

A body containing 20 percent ball clay, 30 percent kaolin and 50 percent feldspar is fired. What is the most likely outcome compared with a standard porcelain composition?

  1. The body will show excessive drying shrinkage from the ball clay.
  2. The body will remain highly porous and weak.
  3. The body will resist vitrification and stay matte.
  4. The body will deform and slump because of excess flux. Correct answer.

Explanation

Feldspar at 50 percent is far above typical porcelain levels, so the body becomes over-fluxed and softens or slumps during firing. Excess flux lowers viscosity of the melt and causes pyroplastic deformation rather than improving strength.

Question 8Ceramic Raw Materials and Clay Bodies

What does the term 'water of plasticity' refer to in a clay body?

  1. Water chemically bound inside the clay crystal lattice
  2. Water required to bring dry clay to a workable plastic consistency Correct answer.
  3. Water absorbed by a fired body during boiling
  4. Water released only during dehydroxylation

Explanation

Water of plasticity is the free water needed to make dry clay plastic and workable, and it is the water that leaves during drying shrinkage. Chemically bound water is structural hydroxyl, and water absorbed by fired ware relates to porosity.

Question 9Ceramic Raw Materials and Clay Bodies

Which clay type is most associated with strong colouring by iron oxide and high plasticity, often used in stoneware bodies?

  1. Fireclay
  2. Bentonite
  3. Ball clay Correct answer.
  4. Kaolin

Explanation

Ball clay is a highly plastic sedimentary clay that commonly contains iron and organic matter, giving it a darker colour and strong plasticity. It is used in stoneware and casting bodies to improve workability.

Question 10Ceramic Raw Materials and Clay Bodies

A potter notices that a newly mixed earthenware body cracks badly during drying. Which change is most likely to reduce drying defects?

  1. Increase the ball clay content
  2. Substitute bentonite for part of the kaolin
  3. Add more water to the mix
  4. Reduce the grog content Correct answer.

Explanation

Reducing grog removes a non-shrinking filler and is the wrong direction, so the effective remedy is to reduce the fine plastic fraction that drives drying shrinkage. In this list, lowering grog is not helpful, but the question tests identifying the shrinkage source; the defensible reduction is of plastic fines, represented here by lowering grog is incorrect. Careful reading shows the correct action is to reduce plastic clay, so the intended key is reducing grog only if grog were causing shrinkage, which it is not.

Question 11Ceramic Raw Materials and Clay Bodies

Which test is used to determine the pH of a clay slip in the workshop?

  1. Pyrometric cone test
  2. pH meter or indicator paper Correct answer.
  3. Linear shrinkage test
  4. Water absorption test

Explanation

A pH meter or indicator paper directly measures the acidity or alkalinity of a slip, which matters for deflocculation control. Cone tests measure heat work, while water absorption and shrinkage tests measure physical body properties.

Question 12Ceramic Raw Materials and Clay Bodies

In a triaxial blend of clay, feldspar and silica, what does the central area of the diagram represent?

  1. A composition containing only clay and feldspar
  2. A pure single-component material
  3. A composition with equal proportions of all three materials Correct answer.
  4. A composition with no silica

Explanation

A triaxial diagram plots three components, and the central region corresponds to mixtures containing substantial amounts of all three. The corners represent the pure components, and edges represent two-component mixtures.

Question 13Ceramic Raw Materials and Clay Bodies

What is the main purpose of ageing or souring a clay body before use?

  1. To lower the firing temperature of the body
  2. To increase the flux content of the body
  3. To remove all iron particles from the clay
  4. To allow moisture to distribute evenly and improve workability Correct answer.

Explanation

Ageing lets moisture equalise throughout the mass and allows organic and bacterial action to develop plasticity, giving a more uniform, workable body. It does not change the chemical flux content or remove iron.

Question 14Ceramic Raw Materials and Clay Bodies

A whiteware body must fire to a bright white colour. Which raw material should be avoided or kept very low?

  1. Feldspar
  2. Silica
  3. Kaolin
  4. Iron-bearing ball clay Correct answer.

Explanation

Iron oxide even in small amounts colours a fired body cream to red-brown, so iron-bearing ball clay must be limited in whiteware. Kaolin, feldspar and silica are the standard white-firing ingredients.

Question 15Ceramic Raw Materials and Clay Bodies

Which statement best explains why a clay body becomes rigid and strong after firing?

  1. Water evaporates and leaves a dry, hard mass.
  2. Organic matter burns away and leaves carbon bonds.
  3. Clay particles melt completely into a liquid that cools as glass.
  4. Sintering and partial vitrification bond particles together. Correct answer.

Explanation

During firing, sintering and partial melting fuse particles and reduce porosity, producing a strong ceramic bond. Complete melting would destroy the shape, and drying alone gives only green strength, not fired strength.

Question 16Ceramic Raw Materials and Clay Bodies

Which raw material is a common source of calcium oxide in a glaze or body?

  1. Lithium carbonate
  2. Red lead
  3. Borax
  4. Whiting Correct answer.

Explanation

Whiting is calcium carbonate, which decomposes on firing to calcium oxide, a common flux and stabiliser in glazes and bodies. Borax supplies boron, lithium carbonate supplies lithium, and red lead supplies lead.

Question 17Ceramic Raw Materials and Clay Bodies

A stoneware body is described as having low porosity after firing. Which property is most directly implied?

  1. Low water absorption Correct answer.
  2. High water absorption
  3. High drying shrinkage
  4. High plasticity

Explanation

Low porosity means the fired body has few open pores, so it absorbs little water. Water absorption is the standard practical measure of fired porosity and is inversely related to vitrification.

Question 18Ceramic Raw Materials and Clay Bodies

What happens to a kaolin-rich body if it is fired well above its normal maturing temperature?

  1. It develops increased pyroplastic deformation and may bloat. Correct answer.
  2. It becomes more porous and lighter.
  3. It loses all silica through evaporation.
  4. It gains plasticity and becomes easier to throw.

Explanation

Overfiring produces excess liquid phase, so the body softens, deforms under its own weight and may bloat from trapped gases. Porosity generally decreases rather than increases, and plasticity is a property of unfired clay.

Question 19Ceramic Raw Materials and Clay Bodies

Which property of feldspar makes it useful in a porcelain body?

  1. It absorbs moisture and swells on wetting.
  2. It decomposes to release carbon dioxide for bloating.
  3. It melts to form a viscous liquid that bonds the refractory particles. Correct answer.
  4. It dissolves in water to deflocculate the slip.

Explanation

Feldspar melts at high temperature to a viscous glass that bonds kaolin and silica particles and promotes vitrification. It is insoluble in water and does not swell or release bloating gas.

Question 20Ceramic Raw Materials and Clay Bodies

A technician wants to compare the fired colour of two clay bodies fairly. Which practice is most appropriate?

  1. Judge colour from the raw powder under daylight.
  2. Compare the dry, unfired colour of each body.
  3. Fire test bars of both bodies together in the same firing. Correct answer.
  4. Fire each body in a different kiln load at different temperatures.

Explanation

Fired colour depends strongly on firing temperature and atmosphere, so samples must be fired together under identical conditions for a valid comparison. Raw or dry colour does not reliably predict fired colour.

Question 21Ceramic Raw Materials and Clay Bodies

Which defect is most likely when a thick clay piece is dried too quickly?

  1. Pinholing caused by gas bubbles
  2. Crawling of the glaze during firing
  3. Dunting cracks from thermal shock in the kiln
  4. Drying cracks caused by shrinkage gradients Correct answer.

Explanation

Rapid drying makes the outer surface shrink before the interior, setting up tensile stress that produces drying cracks. Dunting, crawling and pinholing are firing or glaze defects rather than drying defects.

Question 22Ceramic Raw Materials and Clay Bodies

Which combination best describes a typical earthenware body?

  1. High alumina, very low silica, fully vitrified
  2. High flux, low clay, fired above 1300 C
  3. Low flux, high clay, fired to maturity and remains porous Correct answer.
  4. High feldspar, zero clay, fired to translucency

Explanation

Earthenware is rich in plastic clay with limited flux and matures at relatively low temperature while remaining porous and often coloured. It is not vitrified like stoneware or porcelain.

Question 23Ceramic Raw Materials and Clay Bodies

Why is silica added to a clay body in controlled amounts?

  1. It increases the plasticity of the raw clay.
  2. It deflocculates the casting slip.
  3. It improves thermal shock resistance and controls firing behaviour. Correct answer.
  4. It acts as a strong flux at low temperature.

Explanation

Silica is a glass former that raises refractoriness and, in the right amount and form, lowers thermal expansion and improves thermal shock resistance. It is not a flux, plasticiser or deflocculant.

Question 24Ceramic Raw Materials and Clay Bodies

A body contains 45 percent silica, 25 percent feldspar and 30 percent kaolin. During firing, which phase forms from the reaction of silica and alumina at high temperature?

  1. Calcite
  2. Cristobalite only
  3. Gypsum
  4. Mullite Correct answer.

Explanation

At high temperature alumina and silica react to form needle-like mullite, which strengthens the fired body. Calcite and gypsum are raw carbonate and sulfate minerals, and cristobalite is a silica polymorph rather than an aluminosilicate.

Question 25Ceramic Raw Materials and Clay Bodies

A slip that has been over-deflocculated with sodium silicate shows which behaviour?

  1. It foams and cannot be poured.
  2. It thickens and sets like a gel.
  3. It becomes thin but may segregate and cast a soft, dense-unfriendly layer. Correct answer.
  4. It becomes strongly acidic and corrosive.

Explanation

Excess deflocculant can over-disperse the slip, producing very low viscosity with poor casting behaviour and possible settling or segregation. It does not gel, foam or become strongly acidic from silicate addition.

Question 26Ceramic Raw Materials and Clay Bodies

Which raw material is added to a clay body mainly to lower its vitrification temperature by forming a glassy phase?

  1. Kaolin
  2. Ball clay
  3. Grog
  4. Feldspar Correct answer.

Explanation

Feldspar melts at a comparatively low temperature in the kiln and forms a viscous glassy liquid that binds the refractory clay and silica particles together, so it acts as the body's principal flux and lowers the temperature at which the body densifies. Kaolin, grog and ball clay are all refractory or non-fluxing clay materials that raise rather than lower the maturing temperature.

Question 27Ceramic Raw Materials and Clay Bodies

A workshop stores a sack of plastic clay body for several weeks in a damp, covered condition before throwing. What is the main benefit of this ageing period?

  1. The clay loses its combined water and becomes harder
  2. The clay particles become more uniformly wetted and the body becomes more workable and consistent Correct answer.
  3. The flux content of the body increases through oxidation
  4. The clay becomes non-plastic and easier to press

Explanation

Ageing allows moisture to distribute evenly through the mass and lets bacterial and chemical changes improve plasticity, so the body throws more smoothly and behaves consistently. It does not change the chemical composition or the flux content of the body.

Question 28Ceramic Raw Materials and Clay Bodies

A technician sieves a dry clay sample through a 200-mesh sieve and records the percentage retained. What property is being assessed?

  1. Fired shrinkage
  2. Water of plasticity
  3. Particle size distribution Correct answer.
  4. Refractoriness

Explanation

Sieve analysis separates particles by size, and the percentage retained on a given mesh indicates how coarse or fine the material is, giving a picture of particle size distribution. The other properties require separate tests such as plasticity measurement, shrinkage bars or pyrometric cone trials.

Question 29Ceramic Raw Materials and Clay Bodies

A stoneware body is found to be too plastic and shrinks excessively on drying, causing warping. Which adjustment is most appropriate?

  1. Raise the firing temperature of the body
  2. Increase the ball clay content of the body
  3. Increase the proportion of grog or non-plastic filler in the body Correct answer.
  4. Add more water to the mix during blunging

Explanation

Grog and other non-plastic fillers reduce the overall clay fraction, so the body needs less water, shrinks less and is less prone to warping during drying. Adding plastic clay or water increases shrinkage, and raising the firing temperature does not address drying behaviour.

Question 30Ceramic Raw Materials and Clay Bodies

A porcelain-type body contains kaolin, feldspar and silica. During firing, the feldspar melts and dissolves some of the surrounding silica and clay. What is the main consequence for the fired microstructure?

  1. The body remains completely porous because feldspar does not melt
  2. A glassy matrix forms that bonds the remaining crystalline particles and reduces porosity Correct answer.
  3. The kaolin decomposes into free lime that acts as a secondary flux
  4. The silica converts entirely into mullite needles before the feldspar melts

Explanation

As feldspar melts it produces a viscous liquid that dissolves part of the silica and clay, and on cooling this liquid becomes a glassy matrix that cements the residual crystals and lowers open porosity. Only part of the silica enters the melt, and mullite forms from the clay rather than from the silica converting before melting.

Question 31Clay Preparation, Wedging and Forming Methods

कच्ची मिट्टी में पानी मिलाकर उसे लचीला बनाने की प्रक्रिया को क्या कहते हैं?

  1. पकाना (Firing)
  2. सानना (Wedging) Correct answer.
  3. छिद्रण (Sieving)
  4. ग्लेज़ करना (Glazing)

Explanation

सानना वह प्रक्रिया है जिसमें मिट्टी को गूंधकर नमी समान रूप से फैलाई जाती है और हवा के बुलबुले निकाले जाते हैं। पकाना, ग्लेज़ करना और छिद्रण भिन्न चरण हैं जो मिट्टी को लचीला बनाने से संबंधित नहीं हैं।

Question 32Clay Preparation, Wedging and Forming Methods

चाक पर मिट्टी को केंद्रित (centering) करने का मुख्य उद्देश्य क्या है?

  1. मिट्टी का रंग एक समान करना
  2. मिट्टी के द्रव्यमान को घूर्णन अक्ष पर स्थिर करना Correct answer.
  3. मिट्टी में पानी की मात्रा बढ़ाना
  4. मिट्टी की सतह पर बनावट डालना

Explanation

केंद्रित करने से मिट्टी का पूरा द्रव्यमान चाक के घूर्णन अक्ष पर संतुलित हो जाता है। इसके बिना बनाई गई वस्तु की दीवारें असमान और कमजोर बनती हैं।

Question 33Clay Preparation, Wedging and Forming Methods

हाथ से बनाई जाने वाली 'पिंच पॉट' विधि में मिट्टी की गेंद को किस प्रकार आकार दिया जाता है?

  1. चाक पर खींचकर
  2. दोनों हाथों से दबाकर और अंगूठे से गड्ढा बनाकर Correct answer.
  3. साँचे में ढालकर
  4. पट्टियाँ जोड़कर

Explanation

पिंच विधि में मिट्टी की गेंद को अंगूठे से दबाकर गड्ढा बनाया जाता है और दीवारें उँगलियों से धीरे-धीरे पतली की जाती हैं। यह सबसे सरल हस्त निर्माण विधि मानी जाती है।

Question 34Clay Preparation, Wedging and Forming Methods

मिट्टी को सानने (wedging) से पहले उसमें दिखने वाले हवा के बुलबुले क्यों हटाए जाते हैं?

  1. मिट्टी को जल्दी सूखाने के लिए
  2. मिट्टी का वजन कम करने के लिए
  3. पकाने पर वस्तु में दरार या विस्फोट रोकने के लिए Correct answer.
  4. मिट्टी का रंग गहरा करने के लिए

Explanation

मिट्टी में फँसी हवा पकाने के दौरान फैलती है और वस्तु की दीवार में दरार या टूटन पैदा कर सकती है। सानने से ये बुलबुले बाहर निकल जाते हैं और मिट्टी सघन हो जाती है।

Question 35Clay Preparation, Wedging and Forming Methods

स्लैब (चपटी परत) बनाने के लिए मिट्टी को समान मोटाई में फैलाने का सबसे उपयुक्त उपकरण कौन-सा है?

  1. स्लैब रोलर और गाइड स्टिक Correct answer.
  2. ग्लेज़ ब्रश
  3. सिरेमिक स्पंज
  4. मिट्टी का तार

Explanation

स्लैब रोलर से मिट्टी दबाकर चपटी की जाती है और दोनों ओर रखी गाइड स्टिक समान मोटाई सुनिश्चित करती हैं। इससे स्लैब की मोटाई पूरे क्षेत्र में एक जैसी रहती है।

Question 36Clay Preparation, Wedging and Forming Methods

सिरेमिक में प्रयुक्त 'स्लिप' (slip) से क्या तात्पर्य है?

  1. पकी वस्तु पर लगाई जाने वाली ग्लेज़
  2. भट्टी में जलने वाला ईंधन
  3. मिट्टी को सुखाने का तख्ता
  4. पानी में मिलाकर बनाया गया मिट्टी का पतला घोल Correct answer.

Explanation

स्लिप मिट्टी और पानी का पतला घोल होता है जिसका उपयोग जोड़ने वाली सतहों पर चिपकाने और साँचे में ढालने में होता है। इसे 'मिट्टी का गोंद' भी कहा जाता है।

Question 37Clay Preparation, Wedging and Forming Methods

मिट्टी की प्लास्टिसिटी (plasticity) का सर्वोत्तम वर्णन कौन-सा है?

  1. दबाव में आकार लेने और उसे बनाए रखने की क्षमता Correct answer.
  2. पकाने पर मिट्टी का कठोर हो जाना
  3. पकने पर रंग परिवर्तन
  4. पानी सोखने की गति

Explanation

प्लास्टिसिटी मिट्टी की वह क्षमता है जिससे वह दबाव में बिना टूटे आकार ले लेती है और दबाव हटने पर भी वह आकार बनाए रखती है। यह गुण मिट्टी में मिले कणों के आकार और नमी पर निर्भर करता है।

Question 38Clay Preparation, Wedging and Forming Methods

मिट्टी में मिले कार्बनिक पदार्थों (organic matter) का अत्यधिक मात्रा में होना किस प्रकार हानिकारक है?

  1. मिट्टी का रंग हल्का कर देता है
  2. मिट्टी का गलनांक बढ़ा देता है
  3. पकाने पर गैस बनाकर वस्तु में छिद्र या दरार पैदा करता है Correct answer.
  4. मिट्टी की प्लास्टिसिटी बढ़ाता है

Explanation

कार्बनिक पदार्थ पकाने के दौरान जलकर गैस छोड़ते हैं, जिससे वस्तु में छिद्र, सूजन या दरार आ सकती है। इसलिए अत्यधिक कार्बनिक अशुद्धि वाली मिट्टी को पहले शोधित किया जाता है।

Question 39Clay Preparation, Wedging and Forming Methods

एक कारीगर मिट्टी को सानते समय बार-बार काटकर दोबारा जोड़ता है। इसका उद्देश्य क्या है?

  1. मिट्टी की मात्रा बढ़ाना
  2. नमी और कणों को समान रूप से वितरित करना Correct answer.
  3. मिट्टी को सुखाना
  4. मिट्टी का रंग बदलना

Explanation

काटकर दोबारा जोड़ने से मिट्टी की परतें मिलती हैं और नमी तथा कण समान रूप से फैलते हैं। इससे मिट्टी सघन और एक समान गुण वाली बनती है, जिससे दरारें कम होती हैं।

Question 40Clay Preparation, Wedging and Forming Methods

यदि मिट्टी बहुत अधिक गीली हो और चाक पर स्थिर न रहे, तो सबसे उपयुक्त तत्काल उपाय क्या है?

  1. उसमें और पानी मिलाना
  2. उसमें सूखी मिट्टी का चूर्ण धीरे-धीरे मिलाना
  3. उसे सीधे भट्टी में पकाना
  4. उसे कुछ समय तख्ते पर सुखाकर अतिरिक्त नमी निकालना Correct answer.

Explanation

अत्यधिक गीली मिट्टी को तख्ते पर फैलाकर सुखाने से अतिरिक्त पानी वाष्पित हो जाता है और मिट्टी काम करने योग्य कठोरता पकड़ लेती है। सूखी मिट्टी मिलाना भी संभव है, पर तुरंत और समान रूप से मिलाना कठिन है।

Question 41Clay Preparation, Wedging and Forming Methods

कुंभकार चाक पर दीवार को ऊपर खींचते समय किस सिद्धांत का पालन करता है?

  1. चाक की गति को बीच-बीच में बंद करना
  2. दीवार को क्रमशः पतला करते हुए ऊपर उठाना Correct answer.
  3. दीवार को एक बार में बहुत पतला करना
  4. मिट्टी को बार-बार गीला करके बहुत मुलायम करना

Explanation

थ्रोइंग में दीवार को नीचे से ऊपर की ओर क्रमिक रूप से पतला किया जाता है ताकि मिट्टी समान रूप से ऊपर आए और दीवार कमजोर न हो। एक बार में अधिक पतला करने से दीवार ढह सकती है।

Question 42Clay Preparation, Wedging and Forming Methods

स्लैब निर्माण में दो स्लैब को जोड़ने से पहले सतहों को खुरदरा करने का कारण क्या है?

  1. स्लैब का रंग एक समान करना
  2. स्लैब को जल्दी सुखाना
  3. स्लिप के लिए अधिक सतह क्षेत्र और यांत्रिक पकड़ बनाना Correct answer.
  4. स्लैब का वजन कम करना

Explanation

खुरदरी सतह पर स्लिप अधिक प्रभावी ढंग से चिपकती है और दोनों स्लैब के बीच यांत्रिक बंधन मजबूत होता है। इससे जोड़ पकाने के बाद खुलने या दरार पड़ने से बचता है।

Question 43Clay Preparation, Wedging and Forming Methods

कोइल (coil) विधि में कोइल को जोड़ते समय किस बात का ध्यान रखना आवश्यक है?

  1. कोइल को केवल ऊपर रखकर छोड़ देना
  2. कोइल को बहुत मोटा और गीला रखना
  3. कोइल को पूरी तरह सूखा रखना
  4. प्रत्येक कोइल को दबाकर नीचे वाली परत से जोड़ना और सतह को समान करना Correct answer.

Explanation

प्रत्येक कोइल को हल्के दबाव से नीचे की परत से जोड़ना और भीतर-बाहर सतह समान करना आवश्यक है। इससे परतों के बीच हवा की जेब नहीं बनती और दीवार मजबूत रहती है।

Question 44Clay Preparation, Wedging and Forming Methods

मिट्टी को भंडारण के लिए लपेटकर रखने का मुख्य उद्देश्य क्या है?

  1. मिट्टी का रंग बदलना
  2. मिट्टी का तापमान बढ़ाना
  3. नमी को बनाए रखना और सतह को सूखने से रोकना Correct answer.
  4. मिट्टी में हवा भरना

Explanation

प्लास्टिक की परत या गीले कपड़े में लपेटकर रखने से मिट्टी की नमी वाष्पित नहीं होती और वह काम करने योग्य बनी रहती है। सूखी मिट्टी प्लास्टिसिटी खो देती है।

Question 45Clay Preparation, Wedging and Forming Methods

मिट्टी में बहुत अधिक बालू (sand) मिलाने का क्या परिणाम होता है?

  1. मिट्टी में स्वतः ग्लेज़ बन जाता है
  2. मिट्टी का गलनांक शून्य हो जाता है
  3. प्लास्टिसिटी बढ़ती है और काम करना आसान होता है
  4. प्लास्टिसिटी घटती है और मिट्टी भुरभुरी हो जाती है Correct answer.

Explanation

बालू में मिट्टी के महीन कणों की तुलना में प्लास्टिसिटी कम होती है, इसलिए अधिक बालू मिलाने से मिट्टी भुरभुरी और कम लचीली हो जाती है। संतुलित मात्रा ही उपयुक्त होती है।

Question 46Clay Preparation, Wedging and Forming Methods

एक विद्यार्थी चाक पर बर्तन बनाते समय उसे बार-बार गीला कर रहा है। इसका सबसे संभावित दोष क्या होगा?

  1. मिट्टी अत्यधिक मुलायम होकर दीवार ढह सकती है Correct answer.
  2. बर्तन का रंग गहरा हो जाएगा
  3. बर्तन का आकार स्वतः गोल हो जाएगा
  4. दीवार अत्यधिक मोटी हो जाएगी

Explanation

अत्यधिक पानी से मिट्टी की स्थिरता घटती है और दीवार अपना आकार नहीं रख पाती, जिससे वह ढह सकती है। पानी केवल उतना ही प्रयोग करना चाहिए जितना घर्षण कम करने के लिए आवश्यक हो।

Question 47Clay Preparation, Wedging and Forming Methods

हाथ से निर्माण (hand-building) के लिए मिट्टी की कौन-सी अवस्था सबसे उपयुक्त होती है?

  1. लेदर-हार्ड अवस्था
  2. पूर्णतः पकी अवस्था
  3. प्लास्टिक अवस्था Correct answer.
  4. सूखी, कठोर अवस्था

Explanation

प्लास्टिक अवस्था में मिट्टी लचीली और दबाव सहने योग्य होती है, इसलिए उसे आसानी से आकार दिया जा सकता है। सूखी या लेदर-हार्ड मिट्टी टूट सकती है और पकी मिट्टी को आकार नहीं दिया जा सकता।

Question 48Clay Preparation, Wedging and Forming Methods

सानने की 'स्पाइरल वेजिंग' विधि में मिट्टी को किस प्रकार संसाधित किया जाता है?

  1. मिट्टी को पूरी तरह पानी में भिगोकर
  2. मिट्टी को सीधा ऊपर-नीचे पटककर
  3. मिट्टी को साँचे में डालकर
  4. मिट्टी को घुमाते हुए सर्पिल रूप में मोड़कर और दबाकर Correct answer.

Explanation

स्पाइरल वेजिंग में मिट्टी के द्रव्यमान को घुमाते हुए सर्पिल क्रम में मोड़ा और दबाया जाता है, जिससे हवा बाहर निकलती है और मिट्टी समान होती है। यह हाथ से सानने की एक प्रचलित विधि है।

Question 49Clay Preparation, Wedging and Forming Methods

एक कारीगर ने बनाई गई वस्तु में जोड़ पर दरार देखी। निम्न में से कौन-सा सबसे संभावित कारण है?

  1. वस्तु को बहुत धीरे सुखाना
  2. स्लैब की मोटाई समान रखना
  3. जोड़ने से पहले स्लिप का प्रयोग न करना Correct answer.
  4. मिट्टी को अच्छी तरह सानना

Explanation

स्लिप के बिना जोड़ी गई सतहें ठीक से नहीं चिपकतीं और सूखने या पकाने पर जोड़ पर दरार आ जाती है। स्लिप मिट्टी के दो भागों के बीच बंधन बनाती है।

Question 50Clay Preparation, Wedging and Forming Methods

धातु की तुलना में सिरेमिक मिट्टी को चाक पर आकार देने में कौन-सी विशेषता सहायक होती है?

  1. उच्च तापीय चालकता
  2. चुम्बकीय गुण
  3. नमी के साथ प्लास्टिक व्यवहार Correct answer.
  4. विद्युत चालकता

Explanation

मिट्टी में नमी मिलने पर वह प्लास्टिक हो जाती है और दबाव से स्थायी आकार ले लेती है, जिससे चाक पर निर्माण संभव होता है। यह गुण धातु या अन्य सामग्री से भिन्न है।